| Home | E-Submission | Sitemap | Contact Us |  
Environ Eng Res > Volume 26(3); 2021 > Article
Yuan and Zhu: A review on metal organic frameworks (MOFs) modified membrane for remediation of water pollution

Abstract

Porous metal-organic frameworks (MOFs) have received wide attention on the potential application to separation of pollutants from contaminated water to produce clear water. Recently, the report on MOFs modified membrane in pollution separation is very interesting. The main focus is that adding MOFs onto the surface of the membrane can significantly improve its separation performance and anti-fouling ability. This review took the opportunity to give readers a preliminary and detailing understanding of the basic knowledge of the MOFs modified membrane used in remediation of water pollution.

1. Introduction

According to the World Health Organization (WHO), about 700 million people are still suffering from water shortages around the world, and another 500 million people are on the verge of such a dilemma, what is worse, this situation is expected to be worsen by 2025 [1]. The improvement and development of wastewater treatment technology can effectively alleviate the problem of water shortage. At present, there are many widely used waste water treatment technologies such as adsorption [2], coagulation [3], and biological treatment [4]. Although these traditional water purification technologies have been widely used, their efficiencies in treating water are becoming increasingly inadequate. For example, the cost of activated carbon adsorption in operation is high [5]. It takes a long time and occupies a large area to remove trace organic matters in water and activated sludge by coagulation [6].
With the development of modern biology and physics, membrane technology emerges. The principle of the membrane is to imitate the selective permeability of bioactive cell membrane, that is, the membrane has the property of selective passage of material on both sides [7]. Compared with the traditional wastewater treatment technology, the membrane technology can more effectively remove the color, odor, and organic matter of water, providing a green, efficient and novel method for water or wastewater treatment [8].

1.1. Membrane Technology

In definition, a membrane can be regarded as a selective bottleneck that can prohibit the passage of a certain substance in a complex mixture or solution under a driving force and the driving force can be generated by concentration gradient, pressure gradient or electric field [9]. Most membrane module is composed of one inlet that allows feed passes through and two outlets that are used to pass through permeate and retentate flow, respectively [10].
On the basis of pore configuration, the membrane can be classified into symmetric and asymmetric membrane [11]. Asymmetric membrane has anisotropy, that is, the chemical or physical structure of asymmetric membrane varies with the location of membrane [12]. An asymmetric membrane often consists of three layers: the top layer, the intermediate layer and the support layer. The top layer plays a crucial role in separation processes and can be modified by catalyst or other materials to improve the membrane functions [10]. The support layer supplies the asymmetric membrane with high mechanical strength and the intermediate layer combines the top layer with the support layer as a transition phase, preventing the top layer filtering into the support layer [13].
Using molecular weight cut off (MWCO), the membrane can be classified into four different processes in the membrane technology, including microfltration (MF), ultrafltration (UF), nanofltration (NF) and reverse osmosis (RO) and they are widely used in water purification [14, 15]. The materials for synthesis of membrane mainly include ceramic, polymeric and hybrid materials [16]. Polymer membrane has high selectivity and excellent mechanical strength, which is often used in water purification or desalination process [17]. Compared with polymeric membrane, ceramic membranes have the technical advantages including higher porosity, longer lifetime, better mechanical and chemical stability [18, 19].

1.2. Membrane Fouling

Membrane fouling is a harmful phenomenon that some substances (organic and inorganic components) adhere to the surface or inside of the membrane, which is the crucial problem for membrane technology [20]. It might markedly reduce productivity and permeate quality, leading to higher operating pressure demand, shorter membrane cleaning interval, abbreviated membrane lifespan and higher maintenance cost [21]. Membrane fouling can simply divided into inorganic fouling, biological fouling and organic fouling.
Inorganic pollution is caused by those inorganic particles attached to membrane surface or membrane pore in influent water [22]. It is also called scaling because of the pollution of chemical precipitation or crystallization of multivalent cations such as calcium, magnesium, carbonate, sulfate, and phosphate [23]. The membrane scaling will occur when the ions in the supersaturated solutions crystallize onto the membrane surface through surface crystallization and bulk crystallization [24].
Biological fouling is related to the living microorganisms in the feed water [25]. The bacteria and high-molecular-weight natural polymers as called extracellular polymeric substances secreted by multilayer of living, inactive or dead microorganisms, has a strong connection with biological fouling [26]. Biological fouling not only increases the membrane transport resistance but also biodegrades the selective layer through hydrolysis [25]. Organic fouling mainly results from deposition on the membrane surface or adsorption of organic filth such as proteins, natural organic matters, algogenic organic matter and humic substances [21]. It occurs when membrane have treated a solution contained the organic substances such as oil [27], proteins [28], and humic acid [29], which cling to the membrane surface or embed themselves inside the membrane.
The membrane fouling is affected by the membrane characteristics notably and is harmful to membrane applications [25]. Factors such as pH, salt concentration and membrane structure will cause membrane fouling and affect the membrane technology efficiency [30] so that it is necessary to further improve the separation efficiency and application range of membrane matrix to boost the membrane performance. Therefore, one effective way to alleviate fouling is to introduce antifouling properties to membranes, which can be realized by altering surface hydrophilicity, reducing surface roughness, grafting or coating novel structured polymer and introducing new surface functionalities [31]. Scientists have extensively explored substances that can be packed within the membranes, such as mesoporous silica [32], zeolite [33], and multi-wall carbon nanotubes [34] and mental organic frameworks (MOFs) [35]. Among those materials, the MOFs have attracted extensive attention and been widely researched as a kind of filling material. For instance, Duan et al. [36] successfully gained thin-film nanocomposite (TFN) membrane with ZIF-8 as filler. The study showed that loading 0.05% ZIF-8 on TFN film can increase the water permeability by 88% in the reverse osmosis process. Ma et al. [37] developed a novel filtration membrane with high flux, good solute rejection and excellent antifouling performance by modifying membrane with UiO-66@GO/PES, which showed high water purification performance and superb antifouling performance.
For the past few years, the improvements of membrane technology haven’t stopped. As a nanoparticles introduced into membrane, the MOFs have drawn people’s attention because of their large specific surface area, controllable pore diameter and other superior properties. The combination of the MOF materials as fillers with the membranes can not only improve the efficiency of membrane treatment, but also ensure the reuse of MOFs materials. In this review, various MOFs have been discussed as a filler in the membrane modification. A short introduction to membrane technology, the synthesis method and applications of the MOFs modified membrane have been reviewed.

2. MOFs Types and Synthesis Methods

2.1. Fabrication of MOFs

The MOFs, also known as coordination polymer, are a kind of organic-inorganic hybrid materials, which are different from inorganic porous materials and organic complexes. They have the inorganic porous material’s rigidity and the flexible characteristic as organic material [38, 39]. The MOFs have high specific surface area, and their maximum porosity and pore size are far greater than molecular sieve materials, of which pore size and shape can be controlled by simple methods from micro to mesoporous [40].
The MOFs are mainly utilized in the study of gas storage [41], gas/steam separation [42], selective catalysis [43], the preparation of luminescent materials [44], drug carrier materials [45] and separation [46]. Also, the MOFs have been widely employed to remove heavy metals in water phase [47, 48], such as lead (Pb), arsenic (As), and mercury (Hg). The MOFs can be divided into the different categories: isoreticular metal-organic frameworks (IRMOFs), zeolitic imidazolate frameworks (ZIFs), materials of istitute lavoisier-frameworks (MILs), pocket-channel frameworks (PCNs), and university of Oslo (UiO). The IRMOFs were developed by Yaghi, et al. [49]. They synthesized MOF-5, MOF-74, MOF-177, MOF-199 and IRMOF-0 at room temperature, assembled by organic ligands like various aromatic carboxylic acid with inorganic group [ZnO]6+ in octahedral coordination structures [50]. The ZIFs is usually made of Zn or Co as metal materials with organic materials like imidazoles as ligands, which have excellent thermal and chemical stability [51]. For example, ZIF-8, remained stable under 500°C, which was prepared by zinc nitrate hexahydrate and 2-methyl imidazole in water or N-N-Dimethyl acetamide using hydrothermal synthesis method. There is a broad development space in the fields of gas separation and catalysis for it [52]. In the preparation of MILs, different metal ions, such as chrome, iron, aluminum, vanadium and carboxylic acid ligands like succinic acid or glutaric acid for preparation, which has flexible skeleton and can achieve the channel structure change under different factor influences like temperature, pressure and adsorption materials. Therefore, in the specific adsorption test, the MILs has a great application value so that MIL-53(Cr), MIL-100(Cr), MIL-101 have played an important role in gas storage and separation, catalysis, adsorption, and other fields [5355]. The developed PCN-14 surface area reached 2176 m2/g, of which performance on the methane storage was excellent [56]. The UiO takes zirconium (Zr) for metal material [57]. Among them, UiO-66 is a prominent representative in this series of research, which was synthesized by octahedral [Zr6O4(OH)4] as metal cluster with phthalic acid for organic ligand. Due to its strong coordination effect, UiO-66 has high stability so that it has huge application in the separation and the fluorescent material [58, 59].
There are many types of MOFs synthesis methods [60]. First, the hydrothermal method/solvothermal method uses stainless steel pressure reactor with teflon lining or glass tube to heat mixed raw material solution in the presence of water or organic solvents, gaining high quality single crystal through reaction under inside pressure. MIL-47, MIL-53, MIL-101(Cr) can be synthesized by hydrothermal method, for example, MIL-101(Cr) are synthesized by terephthalic acid and chromium nitrate hydrate in 220°C hydrothermal reactor [61, 62]. Second, the mechanical method makes sharp collision between raw materials’ particles, and the broken particles increase the reagents contact area, effectively reducing the surface activation energy thus being beneficial to the chemical reactions for obtaining good dispersion MOFs. In general, the mechanical method does not need to add other solvents to separate the products and the solvents after synthesis, which ensures the purity of the product and is more conducive to industrialization promotion [63]. Third, microwave method uses the characteristic of raw materials that can quickly absorb electromagnetic waves, then the molecules collide. The polar molecules can achieve the required reaction temperature in a very short period of time, of which preparation is time-effective. The structure and the morphology of MOFs can be controlled by adjusting the parameters of the microwave reaction [64]. Reza et al. [65] successfully synthesized UiO-67 using microwave method, only taking 2 to 2.5 h at 80°C to 150°C, which has a better adsorption capacity for single component (CO2 and CH4). In recent years, many new preparation methods have appeared, such as electrochemical method [66], ultrasonic [67], ionothermal synthesis method [68]. The successful preparation of MOFs modified thin films provides a broader application prospects to MOFs. Compared with the solid MOFs, the MOFs modified membrane has a better application in gas separation, sensors and other fields. Due to the huge demand for the functional MOFs modified porous membrane, invesitgation on their synthesis and applications have been increasing.

2.2. MOFs Modified Membrane

The construction of the MOFs is close related with two areas including molecular sieve membrane synthesized by direct synthesis method or seeding growth method and coordinate polymer membranes like Langmuir-Blodgett membrane or liquid epitaxial film technology [69]. The rich research achievements in the two fields provide the possibility of the gradual combination about the MOFs’ excellent performance and thin films preparation technology.
Two kinds of MOFs modified membranes can be synthesized by certain methods. The first is that the MOFs crystals in the membrane are modified, completely covered on the surface of the carrier or dispersed on the carrier. It is a kind of polycrystalline film that the MOF crystals or particles accumulate on the support surface at any orientation. The other type is the membrane surface crystal growth at a particular direction. There is an interaction between carrier surface and metal organic framework crystals. This MOFs modified membrane has a preferred orientation [7072]. There are many preparation methods of MOFs modified membrane. Different methods and conditions can prepare different pore size, porosity and thickness of membrane. Therefore, the MOFs modified membrane can be prepared by controlling the membrane materials, carriers and preparation methods according to the actual needs. The synthesis method of MOFs modified membrane is similar to that of organometallic matrix powder, but the synthesis conditions are not membrane the same. The direct growth of metal organic skeleton crystal usually requires self-assembled monolayer (SAM) or functionalization of carrier surface by injecting crystal to promote the formation of membrane [73, 74].

2.2.1. In situ crystallization synthesis

In situ crystallization method, also known as direct crystallization method, refers to that under hydrothermal or solvent thermal condition that the carrier is directly in contact with the precursor sol or solution, then metal organic frame crystals produce crystal nucleus near the support body surface because of partial supersaturation. The MOFs modified film is formed by the growth crosslinking of crystal nucleus. In the process of film forming, the crystals grow on the support surface amongst the solution so that the crystal can grow on the support surface in an alternate and consecutive form [75, 76]. The advantages of in situ crystallization synthesis method are simple and convenient with strong applicability and low cost. However, due to the random nucleation on the support surface in mother liquor, in situ crystallization method requires more stringent synthesis conditions. In the process of synthesis, the direction of carrier placement will significantly affect the membrane performance. Most MOFs modified films will generate the multiple layers in the in situ crystallization method to form a thicker membrane, which has an impact on the permeability of gas separation to some extent, but in situ crystallization is still one of the most commonly used methods to synthesize the MOFs modified membrane.
The growth of MOF crystals can be controlled by proper selection of the carrier and surface modification so as to prepare dense and continuous MOFs modified films by in situ crystallization synthesis method. Hermes et al. [77] impregnated SAM containing terminal COOH and CF3 functional group in MOFs reaction solution to synthesize patterned MOF-5 film under conventional solvent-thermal synthesis conditions, which was only deposited on patterned COOH but not on the surface of CF3 functional group. The synthesized MOFs modified film was then placed in a vapor of Cp-allyl-Pd, a precursor of the organic palladium metal. As the powder particles diffused into MOF-5 by steam resulting in color changes, the MOFs modified thin film still presented porosity. The X-ray Diffraction (XRD) data showed that the MOF-5 in the film was equivalent to a conventional MOF-5 material in structure, but the selective deposition on a substrate surface expands the specific preparation and application of a MOFs modified film. In 2015, Al-Maythalony et al. [78] adopted modified porous alumina to prepare the zeolite-like metal organic framework (ZMOF) modified membrane on its substrate by solvent thermal crystallization method for the first time. The membrane had good CO2 osmotic selectivity in gas permeation separation test.

2.2.2. Layer-by-Layer synthesis

Under certain conditions, the carrier can be immersed in the solution of metal ion and organic precursor, respectively. One molecular layer or ion layer at a time grows on the surface of the carrier, and the metal organic framework structure can be controlled to grow in a specific crystal direction by the functional groups modified on the surface of the carrier [79]. This method for obtaining films with preferred orientation is called Layer-by-Layer (LBL) method, as the process is shown in Fig. 1. First, the carrier is immersed in metal ion precursor solution and organic precursor solution, respectively. At certain conditions, one molecular or ion layer forms in the left of the carrier and then it is immersed in the solutions again. After repeating several times, the MOFs modified membrane can be fabricated in the middle of the carrier with specific crystal direction. Shekhah et al. [80] synthesized the crystalline MOFs modified thin films by impregnating matrix in the reaction solution to form the film layer by layer. Xiang et al. [81] made the MOFs modified membrane for gas separation using the layer-by-layer method, of which strong interaction with the membrane filler matrix eliminated the interfacial gap, and the addition of MOF particles improved the selectivity of H2/CO2. Li et al. [82] synthesized the Fe3O4@MOFs and the Fe3O4@MOFs/GO by using the layer-by-layer method, and the results showed that the presence of graphene oxide (GO) increased the drug loading of the magnetic sphere.

2.2.3. Secondary growth synthesis

Second growth method is also known as crystal seed method. This method firstly synthesizes uniform nanometer metal organic framework crystal seeds, after that forming a layer of MOFs crystal seed layer on the surface of the carrier by physical method, then the carrier is put into the synthesis solution with a certain concentration, and finally, it crystallize into the film under certain conditions [8385]. In this method, the seed layer of metal organic framework precoating on the target support usually adopts the physical methods, in which the key step to prepare the MOFs modified film is to form thin and continuous seed layer on the carrier. The simple steps to desply the process are shown in Fig. 2. At the beginning, the MOF crystal seed layer forms on the surface of the carrier by physical method, which is immersed in MOFs modified membrane synthesis solution with a certain concentration. It can fabricate the MOFs modified membrane by crystallization at certain conditions.
Du et al. [86] used nanometer ZIF-8 crystal particles as seed, induced seed growth in α-Al2O3 ceramic tube carrier by secondary growth method, and prepared continuous ZIF-8 modified film. It was found that the ZIF-8 grains on the surface were closely connected without obvious cracks and the thickness of the film was about 18 μm. The separation factor of H2/CH4 and H2/CO2 was 2.56 and 5.4, respectively, which indicated that the membrane had a certain gas separation effect. Zhang et al. [87] prepared an Eu(III)-MOF modified thin films by secondary growth method, which can not only be used as a fluorescence probe for gaseous SO2, but also had a good recyclability and quick response.
The methods for seed deposition also include in situ seed reaction method and high temperature organic ligand deposition, high temperature organic ligand deposition method and others. After the seed layer deposited on the carrier, secondary hydrothermal/ solvent heat treatment can be used to make the seed to form a continuous MOFs modified film [69]. Li et al. [88] obtained continuous and compact ZIF-7 modified films by crystal seed method. Yoo et al. [89] prepared dense MOF-5 crystal layers on porous α-alumina substrates by microwave-induced thermal deposition, and then heat the MOF-5 crystal layers to grow into continuous MOF-5 modified films. Horcajada et al. [90] also prepared porous MIL-89 modified film by colloidal deposition method.

2.2.4. Interface polymerization synthesis

The interfacial polymerization (IP) method is adding two highly reactive monomers in two insoluble solvents and polymerize at insoluble interface to form a very thin dense layer on the porous support [31]. The nanoparticles with specific functions can be fixed on the supporting layer of the polymer separation membrane to prepare a better separation performance membrane [9193]. As a new functional material, the MOFs can be introduced into polymer separation membrane by the interfacial polymerization. The interface polymerization method process is shown in Fig. 3. Two highly reactive monomers are placed in water phase solvent and organic phase solvent, respectively. The reaction occurs only at the interface using the MOFs as support. After washing and dehydration, the MOFs modified membrane is obtained.
Sorribas et al. [94] prepared nano-scale MOFs, including ZIF-8, MIL-53 (Al), NH2-MIL-53 (Al), and MIL-101 (Cr), and formed an MOF interfacial layer on the porous membrane of polyamide (PA) by interfacial polymerization. The interception effect of the synthesized PA-MOF modified film on styrene oligomers in methanol and tetrahydrofuran was tested. The results showed that the styrene oligomer molecules were trapped and the retention rate of PA-MOF membrane to styrene oligomer molecules in the two organic solvents was more than 92%.

2.2.5. Cohybridization synthesis

Cohybridization method is that the matrix and the mother liquor of the modified material are mixed in a certain proportion and then transformed into a film by technical means [95]. The process is showed in Fig. 4. The matrix and mother liquor are mixed in a certain proportion and put in container with a support, which can change into MOFs modified membrane by technical means on the support. This method can not only retain the mechanical properties, chemical stability and thermal stability of the separation membrane materials, but also have the separation or other properties of modified materials, as an important technical mean of polymer separation membrane modification, which has been widely used in the production process [9698]. Many scholars have added the multifunctional MOF material into the polymer membrane material to prepare the polymer MOF modified mixed matrix membrane (MMM) and it is prepared by several process. First, the MOF materials are added into the organic solution, dispersing evenly. After that, the polymer powder is added in it to form polymer membrane. Finally, MMM is gained by scraping and drying the composite membrane. MOF-5 [99], ZIF-8 [100], Cu-BTC [101] and other MOF materials have been reported to be added into polymer membrane materials, and have quite good applications, which enhanced the advantages and characteristics other than MMM in separation. Meera et al. [102] prepared Cu(BDC) MMMs successfully, which exhibited a 70% increase in the CO2/CH4 selectivity.

2.2.6. Other methods

Besides the in-situ crystallization and secondary growth methods mentioned above, there are also novel ways to fabricate MOFs modified films like evaporation control filler positioning method, electrochemical method, and bimetallic source method.
Goethem et al. [103] have developed a new evaporation controlled filler positioning (EFP) technique, of which main purpose is to increase the filler content in the upper layer of the film and its permeability can increase by at least 160% without affecting the salt interception rate [104]. Ameloot et al. [105] used electrochemical method to gain 2~50 μm HKUST-1 modified thin films supported by copper sheet. They sustained process in 55°C temperature and ventilation with N2, and the film was formed on electrochemical anodic. Yang et al. [66] successfully synthesized clear crystalline spherical MOF-5 (IL) by electrochemical method through π-π bond staking effect, ionic bond, coordination bond and other effects, and their crystallization rate and thermal stability were superior to that of the solvent-thermal method.
Bimetal source method means that when the carrier and metal organic framework material have the same metal ions, the surface of the carrier will be oxidized in the reaction process, so as to provide metal ions for the carrier, which is more conducive to the formation of crystal nucleus on the carrier surface [106]. Guo et al. [107] used copper network as the carrier and activated the carrier under 100°C, which was putted in the HKUST-1 reaction liquid at 120°C to prepare uniform continuous membrane modified by HKUST-1.
However, there have been many successful examples of MOFs modified membrane preparation, and there are still some challenges in the film forming property of MOF materials. For example, the instability of MOFs organic part at high temperature, the poor wettability of carrier or other problems are not conducive to the preparation of adding MOFs into films [108]. For the membrane stability, there is a lack of effective interface interaction between the MOFs and the membrane support [77, 109], so it is necessary to explore a method to enhance the interaction between the MOFs and the carrier. One of the feasible methods is to construct graphite-spun coating on the porous carrier to enhance the interface interaction between them, for instance, IRMOF-1 grown on AAO carrier was easy to fall off under ultrasonic condition, while IRMOF-1 film on AAO carrier preparation by graphite coating still had about 80% coverage after ultrasonic 1 hour [110]. In addition, the carrier modified by alkylation reagents [111], the MOF precursor chemical [112] or polymer binders [113] can improve the dependence of the MOF crystals on the porous carrier. If the MOFs modified membrane synthesis method is not properly selected, it will lead to unstable adhesion of the MOF materials on the membrane or cause interface collapse and other problems easily.
Secondary effects in the preparation process of metal organic framework films also hinder the formation of MOFs modified film, which are caused by many complex reasons and play an important role, although it may not the dominate effect [103]. Lind et al. [114] showed that in the process of interfacial polymerization, some filler particles, once in contact with water, would immediately underwent hydration reaction and generated local heat, thus affecting the reaction kinetics of interfacial polymerization and the miscibility of solvents. In addition to the hydration reaction between filler particles and water phase, particle fragments and MOFs degradation products may also appear at the interface during IP process and the main reason is that the most common condensation polymerization reaction between chloric acid and diamine will lead to the formation of HCl in the IP process, which has a high degree of locality and rapidity so that the local pH will drop greatly, while the ZIF-8 is considered relatively stable, will degrade at a pH of 5 [115, 116]. On this occasion, one method can be adopted is to add sodium hydroxide. Since sodium hydroxide is added to the aqueous solution, the function of deprotonated alcohol can increase the reactivity and the IP reaction only forms NaCl as a by-product, what is more, the MOFs fillers such as ZIF-8 can remain stable under alkaline conditions [103, 117]. This article showed an overview about MOFs and MOFs modified membrane, including their synthesis methods, applications, which is shown in Fig. 5.

3. Typical Applications in Water Treatment

The MOFs modified membranes have been widely used in gas separation [118], catalysis [119], sensing [120], water purification [121] and other fields due to its superior performance. Ilknur et al. [122] assessed 172 different MOFs about CH4/H2 separation performances in membrane forms by atomically-detailed simulations aiming to find the most promising membrane materials. The results showed that most of the MOFs modified membranes exhibited high CH4 selectivity over H2 and a small number of MOF modified membranes exhibited ordinary H2 and CH4 selectivity. What was more, several MOFs were identified to exceed the upper bound established for polymeric membranes and many MOFs modified membranes showed higher gas permeabilities and selectivities. Sun et al. [123] introduced a novel metal organic framework MOF-801 nanocrystal into polyether-block-amide (PEBA) polymer to fabricate a new mixed-matrix material for CO2 separation.
Ramos et al. [124] used cylindrical cordierite as the base material and prepared MIL-101 (Cr) modified membrane by crystal seed method, which could be used as a catalyst for catalytic oxidation of tetrahydronaphthalene. Deng et al. [125] prepared PFSA/ZIF-8 composite membranes and PFSA/MIL-101 composite membranes for proton exchange membrane fuel cells. The two kinds of water stabilized MOFs grew on perforated stainless steel mesh surface modified by polydopamine (PDA) or polydopamine/Polyetherimide (PDA/PEI). Thanks to the good water absorption ability and thermal stability of the MOF layer, which is conducive to proton transfer and water management under high temperature and dry conditions, the power density of PFSA/ZIF-8 composite membrane and PFSA/MIL-101 composite membrane of proton exchange membrane fuel cell was three times higher than max power density of the commercial membrane in 60°C. Cheng et al. [126] fabricated nanohybrid MOFs modified membrane by FeIII-HMOF-5 and sodium alginate (SA) matrix. The introduction of FeIII iron increased coordinatively unsaturated sites which can improve the solubility selectivity because of its preferential dissolution of water molecules over ethanol molecules and the FeIII-HMOF-5 composite membrane possessed the best separation performance with the 1540 g/m2 h of permeation flux when using dehydration of 90 wt% ethanol aqueous solution in model system, which was better than pure SA membrane and the hybrid membranes incorporating hollow MOF-5 (HMOF-5) or MOF-5. Yang et al. [127] prepared cellulose acetate (CA)/MOF@GO membranes to enhance CA membrane performance and studied its characters. The hybrid membrane exhibited higher hydrophilicity, flux recovery ratio, pure water flux and better antifouling performance because the introduced HKUST-1 can fully make use of the structure advantages of GO and prevent GO layers stacking, which showed great potential in water purification applications.

3.1. Desalting

Desalting is a process to produce potable water or high purity water for industrial by removing salt ions from a saline source [128] using membrane technology. It is an available option to use the MOFs modified membrane. Some efforts have been devoted to the application.
Lee et al. [129] used C300, a kind of MOF based material, as removable fillers to create porous matrix membranes, which had the best dissoluvability compared with other 2 kind of MOFs and showed higher porosity, better hydrophilicity and lower tortuosity, leading to water flux increase but a slight decrease in salt rejection. At the same time, UiO-66 particles were usually used in TFN membranes as hydrophilic fillers for forward osmosis desalination. Ma et al. [130] took this way and found that the more nanoparticles (NPs) loaded, the thicker the membrane was, with the decreased contact angle. The high NPs loading ratio decreased the flux and the salt rejection was maintained almost due to the small pore size of UiO-66, which did not allow hydrated Na+ and Cl ions to pass through.
Mil-101 (Cr) nanoparticles were prepared and embedded into the TFN membrane to improve their permeability by Xu et al. [131]. The results showed that the optimal addition amount of nanoparticles was 0.05 wt%, and compared with the ordinary membrane with a flux of 2.2 L/(m2·h·bar), the water flux increased by 44%, while the NaCl retention rate remained 99%. Liu et al. [132] fabricated 2 μm thickness UiO-66 modified thin film membrane by solvothermal method for desalination. The results showed that the membrane had high salt rejection toward multivalent ions, with a relatively high permeability because the UiO-66 aperture diameter was between water molecule and many hydrated ions [133].

3.2. Removing Heavy Metal

Some toxic metal elements are easy to harm human, which have received wide attention due to recalcitrance and persistence in the environment [134]. In recent years, the MOF membranes have been utilized in removing some toxic metal elements.
Yuan et al. [135] fabricated a novel ZIF-300 MOF membrane for removing heavy metal ions from wastewater. The prepared ZIF-300 membrane showed high and stable performance with 99.21% CuSO4 rejection rate. Sana et al. [136] synthesized UiO-66-NH2 MOF through microwave heating method and incorporated it into the polyacrylonitrile (PAN) /chitosan nanofibers for removing Pb(II), Cd(II) and Cr(VI) ions. The results showed that the membrane had higher water flux and metal ions removal rate in aqueous solutions and its adsorption mechanism matched the Pseudo-second-order kinetic and Redlich-Peterson isotherm model, which had great potential for the removal of metal ions from aqueous solutions with filtration time less than 18h. Johnson et al. [137] embedded MOF-808 in nanofibrous membranes and studied the removal of heavy metal (lead, Pb) ions by membrane adsorption/filtration. The experiment obtained S-shaped breakthrough curves about the heavy metal concentration and the filtration period. The simple model could matched the data well and revealed that the parameters involved in the model equations were correlated to the properties of mixed matrix nanofibrous membranes, including the pore size and pore size distribution, membrane thickness, fiber diameter, the adsorption rate constant, the Langmuir adsorption constant and the maximum adsorption capacity, which benefited the design of heavy metal ions removal process. Yin et al. [138] first combined MOF with ceramic membrane ultrafiltration (CUF) successfully for Pb (II) removal from wastewater. The results showed that the MOFs can be stored (100%) when the membrane had an average pore size of 50 nm. The CUF process performed best that the Pb (II) removal rate was 61.4% with lowest flux decline and lowest degree of membrane fouling at the conditions of 0.15 MPa trans-membrane pressure and 4.0 m·s−1 cross-flow velocity in 35°C. What was more, the membrane adsorption capacity was 1795.3 mg·g−1 at equilibrium and the flux exhibits a recovery efficiency near 100% after 6 cycles by using 0.5% (w/w) ammonium citrate followed by 0.5% (w/w) HNO3 solution and each cleaning for an hour at 18–50°C.

3.3. Aqueous Organic Matter Separation

Organic matter removal is a fundamental process in sewage treatment [139] and membrane technology provides a low energy cost and high efficient way to treat it [125].
Jin et al. [140] took polyvinylidene fluoride (PVDF) nanofibrous substrate as supporter to form a high efficient MMM by embedding ZIF-8 into polydimethylsiloxane (PDMS) for phenol removal in aqueous phase membrane extraction process and it showed extraordinary high overall mass-transfer coefficient, which was much better than pristine membrane in the membrane extraction process and the high performance was kept after over 360 h without loss of salt rejection. Li et al. [141] incorporated hydrophilic MOF-801 crystals into chitosan (CS) matrix to fabricate MOF-801/CS MMMs for pervaporation dehydration of ethanol. MOF-801 was proved to restrain the diffusion of ethanol molecules by free volume and the lowest energy sorption sites analyses and provide additional transport pathways for water molecules, which achieved higher flux and separation factor so that the 4.8 wt% MOF-801 loading membrane could reach 1937 g/m2 h the total flux of and 2156 separation factor. Mao et al. [142] prepared ZIF-8 MMMs through interfacial synthesis for ethanol permselective pervaporation and the membrane exhibited the increase in permeation flux, separation factor and good anti-tradeoff effect when used for ethanol recovery from aqueous solution and better pervaporation performance with high permeation flux and comparable separation factor in separating 5.0 wt% ethanol aqueous solution at 40°C. Gao et al. [143] utilized Eu(BTB)(H2O)2·solvent]n(EuBTB), a kind of lanthanide-based two-dimensional MOFs, and sodium alginate (SA) to prepare hybrid membranes for organic solvent dehydration. Because of the strong interfacial interaction between EuBTB and SA through carboxylic groups, the hybrid membranes showed high mechanical strength and swelling resistance. At the same time, it exhibited superior permeability and ethanol dehydration selectivity, which performed best when containing 5 wt% EuBTB with permeation flux of 1996 g/m2 h and separation factor of 1160 for 90 wt% ethanol aqueous solution at 350 K [129]. Neus et al. [144] prepared C-MIL-125-15-NH2 and incorporated it into mechanically stable membranes, which performed well in extraction. The hybrid material showed excellent performance in separating mixtures of bisphenol A (BPA) and 4-tert-butylphenol (4-tBP), facilitating their determination when present at low concentration levels. Alexandra et al. [145] adopted MOF-5 seed crystals to prepare MOF-5 modified membranes about 10 μm thick with high quality by the secondary growth method. Although the membrane would be permanent fouled upon exposure to xylene stream so that there existed a permanent reduction in permeation flux, it was stable in organic solvent and could be used for liquid organic molecules separation based on the molecular sieving effects. Kang et al. [146] gained MMMs successfully by incorporating microporous ZIF-7 crystal particles into chitosan (CS) membrane for separating mixtures of water/ethanol at 25°C during pervaporation process. The ZIF-7/CS modified membranes revealed better capability in separation factor and flux than CS based membranes and MMMs. What’s more, MMMs with 5 wt% ZIF-7 showed the best separation efficiency than pristine CS membranes due to the rigidified polymer chain of MMMs [132]. Tan et al. [147] fabricated MIL-68(Al)/PVDF through mixing the MIL-68(Al) nanoparticles and PVDF casting solution for the first time, which was used to eliminate p-nitrophenol (PNP) and methylene blue (MB). In their study, all the hybrid membranes showed better adsorption capacity than pristine PVDF and the process was mainly characterized by Langmuir monolayer adsorption and chemical adsorption. The highest removal efficiency of PNP and MB might contribute to the coordination bonding between −NO2 of PNP with Al3+ of MIL-68(Al) and the acid-base interaction between the sulfur of MB and Al3+ of MIL-68(Al). D. Ragab et al. [148] modified polytetrafluoroethylene (PTFE) double layer microfiltration membrane with ZIF-8 for micropollutants removal from water, using progesterone as a model pollutant. With the incorporation of ZIF-8 onto the polymer matrix, the membrane adsorption capacity increased close to 40% and almost doubling its water permeability with a significant reduction in processing specific energy consumption, which also maintained near 95% of its original removal efficiency after three regeneration cycles using polyethylene glycol-400 [134].

4. Conclusions

It is a feasible choice to improve the performance of the membrane by coupling with the MOF materials. The properties of the membrane and the purpose for which it will be used determine the methods and types of the MOFs synthesis. It is able to enhance the membrane performance such as stability. However, the membrane still needs to improve: the instability of the organic ligands in the MOFs at high temperature as well as the poor interaction between the MOF materials and the membrane, which is likely to lead to the easily falling off of MOFs, a secondary effect and an interface collapse after the completion of the membrane modification, thus selecting an appropriate method to modify the membrane is important. The modified membrane in various fields shows an excellent performance. However, the MOFs modified membrane is still observed in laboratory scale. How to bring it to an industrial scale is still expected.

Acknowledgment

This work is financially supported by key-Area Research and Development Peogram of Guangdong Province, China (No. 2019B110205001), Natural Science Foundation of Hunan Province of China (No. 2018JJ2128), and China Postdoctoral Science Foundation (No. 2017M622578).

Notes

Author Contributions

Y.Q. (M.S. student) wrote the manuscript. Z.G. (Associate Professor) designed the review and revised the manuscript.

References

1. Organization World Health. International decade for action Water For Life, 2005–2015. Wkly Epidemiol Record. 2005;80:195–200.


2. Qu W, Yuan T, Yin G, Xu S, Zhang Q, Su H. Effect of properties of activated carbon on malachite green adsorption. Fuel. 2019;249:45–53.
crossref

3. Ma B, Xue W, Hu C, Liu H, Qu J, Li L. Characteristics of microplastic removal via coagulation and ultrafiltration during drinking water treatment. Chem Eng J. 2019;359:159–167.
crossref

4. Li N, Liu Q, Zhou G, Dai M, Kong Q. Contaminant removal and microorganism response of activated sludge in sulfamethazine wastewater treatment. Int Biodeterior Biodegrad. 2019;143:104705.
crossref

5. Tian Ting. Study on Three-phase Internal Loop Biological Fluidized Bed Tecgboligy of Oily Wastewater [dissertation]. Qingdao: Ocean University of China; 2013.


6. Wang Y. Ultrafiltration System in Waterworks in Upgrading Pilot Study and Application [dissertation]. Lanzhou: Lanzhou University of Science and Technology; 2011.


7. Shaozhuang N. Membrane Separation Technology in Beverage. China Food Ind. 2005;5:34.


8. Laîné JM, Vial D, Moulart P. Status after 10 years of operation — overview of UF technology today. Desalination. 2000;131:17–25.
crossref

9. Issaoui M, Limousy L. Low-cost ceramic membranes: Synthesis, classifications, and applications. C R Chim. 2019;22:175–187.
crossref

10. Thakur VK, Voicu SI. Recent advances in cellulose and chitosan based membranes for water purification: A concise review. Carbohydr Polym. 2016;146:148–165.
crossref

11. Voicu SI, Stanciu ND, Nechifor AC, Vaireanu DI, Nechifor G. Synthesis and characterization of ionic conductive polysulfone composite membranes. Rom J Inf Sci Tech. 2009;12:410–422.


12. Goei R, Lim T. Asymmetric TiO2 hybrid photocatalytic ceramic membrane with porosity gradient: Effect of structure directing agent on the resulting membranes architecture and performances. Ceram Int. 2014;40:6747–6757.
crossref

13. Lindqvist K, Lidén E. Preparation of alumina membranes by tape casting and dip coating. J Eur Ceram Soc. 1997;17:359–366.
crossref

14. Ihsanullah , Amer AMA, Laoui T, Hilal N, et al. Fabrication and antifouling behaviour of a carbon nanotube membrane. Mater Des. 2016;89:549–558.
crossref

15. He Z, Lyu Z, Gu Q, Zhang L, Wang J. Ceramic-based membranes for water and wastewater treatment. Colloids Surf A. 2019;578:123513.
crossref

16. Ihsanullah . Carbon nanotube membranes for water purification: Developments, challenges, and prospects for the future. Sep Purif Technol. 2019;209:307–337.
crossref

17. Zhang W, Zhang Y, Fan R, Lewis R. A facile TiO2/PVDF composite membrane synthesis and their application in water purification. J Nanopart Res. 2016;18:1–10.
crossref pdf

18. Padaki M, Surya MR, Abdullah MS, Ismail AF, et al. Membrane technology enhancement in oil–water separation. A review. Desalination. 2015;357:197–207.
crossref

19. Hofs B, Ogier J, Vries D, Beerendonk EF, Cornelissen ER. Comparison of ceramic and polymeric membrane permeability and fouling using surface water. Sep Purif Technol. 2011;79:365–374.
crossref

20. Mikhaylin S, Bazinet L. Fouling on ion-exchange membranes: Classification, characterization and strategies of prevention and control. Adv Colloid Interface Sci. 2016;229:34–56.
crossref

21. Liao Y, Bokhary A, Maleki E, Liao B. A review of membrane fouling and its control in algal-related membrane processes. Bioresour Technol. 2018;264:343–358.
crossref

22. Wang Z, Ma J, Tang CY, Kimura K, Wang Q, Han X. Membrane cleaning in membrane bioreactors: A review. J Membr Sci. 2014;468:276–307.
crossref

23. Shirazi S, Lin C, Chen D. Inorganic fouling of pressure-driven membrane processes — A critical review. Desalination. 2010;250:236–248.
crossref

24. Warsinger DM, Swaminathan J, Guillen-Burrieza E, Arafat HA, Lienhard VJH. Scaling and fouling in membrane distillation for desalination applications: A review. Desalination. 2015;356:294–313.
crossref

25. Goh PS, Lau WJ, Othman MHD, Ismail AF. Membrane fouling in desalination and its mitigation strategies. Desalination. 2018;425:130–155.
crossref

26. Yu W, Yang Y, Graham N. Evaluation of ferrate as a coagulant aid/oxidant pretreatment for mitigating submerged ultrafiltration membrane fouling in drinking water treatment. Chem Eng J. 2016;298:234–242.
crossref

27. Chaabane L. Ageing of ion-exchange membranes used in an electrodialysis for food industry: SEM, EDX, and limiting current investigations. Desalin Water Treat. 2015;56:2561–2566.
crossref

28. Ruiz B, Sistat P, Huguet P, Pourcelly G, Araya-Farias M, Bazinet L. Application of relaxation periods during electrodialysis of a casein solution: Impact on anion-exchange membrane fouling. J Membr Sci. 2007;287:41–50.
crossref

29. Lindstrand V, Sundström G, Jönsson A. Fouling of electrodialysis membranes by organic substances. Desalination. 2000;128:91–102.
crossref

30. Liu Z, Xu S, Li S. Membrane Fouling And Cleaning in UF And MF. Technol Water Treat. 1997;22:3–9.


31. Jeong B, Hoek EMV, Yan Y, et al. Interfacial polymerization of thin film nanocomposites: A new concept for reverse osmosis membranes. J Membr Sci. 2007;294:1–7.
crossref

32. Yan W, Shi M, Wang Z, et al. Amino-modified hollow mesoporous silica nanospheres-incorporated reverse osmosis membrane with high performance. J Membr Sci. 2019;581:168–177.
crossref

33. Zhu M, Huang S, Gong Y, et al. Effect of flouride on preparation and pervaporation performance of NaY zeolite membrane for EtOH/ETBE mixture. Microporous Mesoporous Mater. 2019;282:48–52.
crossref

34. Zhou R, Rana D, Matsuura T, Lan CQ. Effects of multi-walled carbon nanotubes (MWCNTs) and integrated MWCNTs/SiO2 nano-additives on PVDF polymeric membranes for vacuum membrane distillation. Sep Purif Technol. 2019;217:154–163.
crossref

35. Lau WJ, Stephen G, Matsuura T, Emadzadeh D, Paul JC, Ismail AF. A review on polyamide thin film nanocomposite (TFN) membranes: History, applications, challenges and approaches. Water Res. 2015;80:306–324.
crossref

36. Duan J, Pan Y, Pacheco F, Litwiller E, Lai Z, Pinnau I. High-performance polyamide thin-film-nanocomposite reverse osmosis membranes containing hydrophobic zeolitic imidazolate framework-8. J Membr Sci. 2015;476:303–310.
crossref

37. Ma J, Guo X, Ying Y, Liu D, Zhong C. Composite ultrafiltration membrane tailored by MOF@GO with highly improved water purification performance. Chem Eng J. 2017;313:890–898.
crossref

38. Seoane B, Castellanos S, Dikhtiarenko A, Kapteijn F, Gascon J. Multi-scale crystal engineering of metal organic frameworks. Coord Chem Rev. 2016;307:147–187.
crossref

39. Li W, Zhang Y, Li Q, Zhang G. Metal–organic framework composite membranes: Synthesis and separation applications. Chem Eng Sci. 2015;135:232–257.
crossref

40. Elsaidi SK, Mohamed MH, Banerjee D, Thallapally PK. Flexibility in Metal–Organic Frameworks: A fundamental understanding. Coord Chem Rev. 2018;358:125–152.
crossref

41. Langmi HW, Ren J, North B, Mathe M, Bessarabov D. Hydrogen Storage in Metal-Organic Frameworks: A Review. Electrochim Acta. 2014;128:368–392.
crossref

42. Finsy V, Ma L, Alaerts L, Vos DED, Baron GV, Denayer JFM. Separation of CO2/CH4 mixtures with the MIL-53(Al) metal–organic framework. Microporous Mesoporous Mater. 2009;120:221–227.
crossref

43. Chen YZ, Zhang R, Jiao L, Jiang HL. Metal–organic framework-derived porous materials for catalysis. Coord Chem Rev. 2018;362:1–23.
crossref

44. Xu X, Guo Y, Wang X, et al. Sensitive Detection of Pesticides by a Highly Luminescent Metal-organic Framework. Sens Actuators, B. 2018;260:239–245.
crossref

45. Lei Z, Yan C, Rui S, et al. Synthesis of hollow nanocages MOF-5 as drug delivery vehicle to solve the load-bearing problem of insoluble antitumor drug oleanolic acid (OA). Inorg Chem Commun. 2018;96:20–23.
crossref

46. Hao L, Wang K, Sun Y, Lollar CT, Li J, Zhou HC. Recent advances in gas storage and separation using metal–organic frameworks. Mater Today. 2017;2017:108–121.


47. Wen J, Fang Y, Zeng G. Progress and prospect of adsorptive removal of heavy metal ions from aqueous solution using metal–organic frameworks: a review of studies from the last decade. Chemosphere. 2018;201:627–643.
crossref

48. Xiong N, Wan P, Zhu G, et al. Sb(III) removal from aqueous solution by a novel nano-modified chitosan (NMCS). Sep Purif Technol. 2020;236:116266.
crossref

49. Morris W, Taylor RE, Dybowski C, Yaghi OM, Garcia-Garibay MA. Framework mobility in the metal–organic framework crystal IRMOF-3: Evidence for aromatic ring and amine rotation. J Mol Struct. 2011;1004:94–101.
crossref

50. Tranchemontagne DJ, Hunt JR, Yaghi OM. Room temperature synthesis of metal-organic frameworks: MOF-5, MOF-74, MOF-177, MOF-199, and IRMOF-0. Tetrahedron. 2008;64:8553–8557.
crossref

51. Safaei M, Foroughi MM, Ebrahimpoor N, Jahani S, Omidi A, Khatami M. A review on metal-organic frameworks: Synthesis and applications. TrAC, Trends Anal Chem. 2019;118:401–425.
crossref

52. Pokhrel J, Bhoria N, Anastasiou S, et al. CO2 adsorption behavior of amine-functionalized ZIF-8, graphene oxide, and ZIF-8/graphene oxide composites under dry and wet conditions. Microporous Mesoporous Mater. 2018;267:53–67.
crossref

53. Adhikari AK, Lin KS, Tu MT. Hydrogen storage capacity enhancement of MIL-53(Cr) by Pd loaded activated carbon doping. J Taiwan Inst Chem Eng. 2016;63:463–472.
crossref

54. Ying M, Hui Q, Gan Y, et al. Green and time-saving synthesis of MIL-100(Cr) and its catalytic performance. Microporous Mesoporous Mater. 2019;274:70–75.
crossref

55. Thanh HTM, Phuong TTT, Hang PTL, et al. Comparative study of Pb(II) adsorption onto MIL-101 and Fe–MIL–101 from aqueous solutions. J Environ Chem Eng. 2018;6:4093–4102.
crossref

56. Sun H, Zhang J, Ouyang C, Ren Z, Li J. Computational evaluation of the impact of metal substitution on the 14CH4 storage in PCN-14 metal-organic frameworks. Catal Today. 2018;312:168–173.
crossref

57. Chen S, Lin Z, Zhao Z, et al. Study on Desorption Process of n-Heptane and Methyl Cyclohexane Using UiO-66 with Hierarchical Pores. Acs Appl Mater Interfaces. 2018;10:21612–21618.
crossref

58. Zhao S, Chen D, Xu H, et al. Combined effects of Ag and UiO-66 for removal of elemental mercury from flue gas. Chemosphere. 2018;197:65–72.
crossref

59. Jin L, Xu F, Jing H, et al. Preconcentration on metal organic framework UiO-66 for slurry sampling hydride generation-atomic fluorescence spectrometric determination of ultratrace arsenic. Microchem J. 2017;133:441–447.
crossref

60. Yongning B, Nana X, Guocheng Z. Technology for the Remediation of Water Pollution: A Review on the Fabrication of Metal Organic Frameworks. Processes. 2018;6:122.
crossref

61. Wang X, Jacobson AJ. Hydrothermal crystal growth and Vernier structures of the metal benzenedicarboxylates MIL-47 and MIL-53 containing guest molecules of benzenecarboxylic acid. J Solid State Chem. 2016;236:230–235.
crossref

62. Yang LT, Qiu LG, Hu SM, Jiang X, Xie AJ, Shen YH. Rapid hydrothermal synthesis of MIL-101(Cr) metal–organic framework nanocrystals using expanded graphite as a structure-directing template. Inorg Chem Commun. 2013;35:265–267.
crossref

63. Ma J. Fabrication and Separation Performance of Nanoporous Materials Based Mixed Matrix Membranes [dissertation]. Beijing: Beijing University of Chemical Technology; 2017.


64. Isaeva VI, Kustov LM. Microwave activation as an alternative production of metal-organic frameworks. Russ Chem Bull. 2016;65:2103–2114.
crossref pdf

65. Vakili R, Xu S, Al-Janabi N, Gorgojo P, Holmes SM, Fan X. Microwave-assisted synthesis of zirconium-based metal organic frameworks (MOFs): Optimization and gas adsorption. Micropor Mesopor Mater. 2018;260:45–53.
crossref

66. Yang HM, Liu X, Song XL, Yang TL, Liang ZH, Fan CM. In situ electrochemical synthesis of MOF-5 and its application in improving photocatalytic activity of BiOBr. Chin J Catal. 2015;25:3987–3994.
crossref

67. Abuzalat O, Wong D, Elsayed M, Park S, Kim S. Sonochemical Fabrication of Cu(II) and Zn(II) Metal-Organic Framework Films on Metal Substrates. Ultrason Sonochem. 2018;45:180–188.
crossref

68. Olorunyomi JF, Chan KY, Gao L, Voskanyan A, Li CYV. Direct synthesis of anion-exchange polymer threaded in a metal organic framework through in situ polymerization of an ionic liquid. Micropor Mesopor Mater. 2017;259:255–263.
crossref

69. Zhang F, Sun FX, Zhu GS. Preparation and application of metal-organic framework films. Sci Sin. 2013;43:1748–1760.


70. Rob A, Elena G, Hiroshi UI, et al. Direct patterning of oriented metal-organic framework crystals via control over crystallization kinetics in clear precursor solutions. Adv Mater. 2010;22:2685–2688.
crossref

71. Tu L, Zheng XL, Lee HL. A Biomimetic Nose by Microcrystals and Oriented Films of Luminescent Porous Metal–Organic Frameworks. Cryst Growth Des. 2011;11:4146–4154.
crossref

72. Katsuhiko K, Rie H, Osami S, Mamoru Y, Yasuyuki A, Hiroshi K. Construction of highly oriented crystalline surface coordination polymers composed of copper dithiooxamide complexes. J Am Chem Soc. 2008;130:15778–15779.
crossref

73. Allara DL, Nuzzo RG. Spontaneously Organized Molecular Assemblies. 1. Formation, Dynamics, and Physical Properties of n-Alkanoic Acids Adsorbed from Solution on an Oxidized Aluminum Surface. Langmuir. 1985;1:45–52.
crossref

74. Bo L, Mingyan M, Denise Z, et al. Chemistry of SURMOFs: layer-selective installation of functional groups and post-synthetic covalent modification probed by fluorescence microscopy. J Am Chem Soc. 2011;133:1734–1737.
crossref

75. Shah M, Kwon HT, Tran V, Sachdeva S, Jeong HK. One step in situ synthesis of supported zeolitic imidazolate framework ZIF-8 membranes: Role of sodium formate. Microporous Mesoporous Mater. 2013;165:63–69.
crossref

76. Li Z, Zhang M, Xue W, Qiu L. In situ Preparation of Metal organic Frameworl [Zn(BDC)(H2O)2]n Films and Reversible Detection of Nitrobenzenes. Chin J Lumin. 2011;32:514–518.
crossref

77. Stephan H, Felicitas SD, Rolf C, Christof WL, Fischer RA. Selective nucleation and growth of metal-organic open framework thin films on patterned COOH/CF3-terminated self-assembled monolayers on Au(III). J Am Chem Soc. 2005;127:13744–13745.
crossref

78. Al-Maythalony BA, Osama S, Raja S, Youssef B, Ingo P, Mohamed E. Quest for anionic MOF membranes: continuous sod-ZMOF membrane with CO2 adsorption-driven selectivity. J Am Chem Soc. 2015;137:1754–1757.
crossref

79. Lee D, Li Q, Kim H, Lee K. Preparation of Ni-MOF-74 membrane for CO2 separation by layer-by-layer seeding technique. Micropor Mesopor Mater. 2012;163:169–177.
crossref

80. Osama S, Hui W, Stefan K, et al. Step-by-step route for the synthesis of metal-organic frameworks. J Am Chem Soc. 2007;129:15118–15119.
crossref

81. Xiang F, Marti AM, Hopkinson DP. Layer-by-layer assembled polymer/MOF membrane for H2/CO2 separation. J Membr Sci. 2018;556:146–153.
crossref

82. Li L, Sun KK, Fan L, Hong W, Xu ZS, Liu L. Layer by layer assembly synthesis of Fe3O4@MOFs/GO core–shell nanoparticles. Mater Lett. 2014;126:197–201.
crossref

83. Zou X, Zhang F, Thomas S, Zhu G, Valtchev V, Mintova S. Co3(HCOO)6 Microporous Metal–Organic Framework Membrane for Separation of CO2/CH4 Mixtures. Chem Eur J. 2011;17:12076–12083.
crossref

84. Zhou S, Zou X, Sun F, et al. Challenging fabrication of hollow ceramic fiber supported Cu3(BTC)2 membrane for hydrogen separation. J Mater Chem. 2012;22:10322–10328.
crossref

85. Zhao Z, Zhong LI, Yslin J. Secondary growth synthesis of MOF-5 membranes by dip-coating nano-sized MOF-5 seeds. CIESC J. 2011;62:507–514.


86. Du S, Liu Y, Kong L, Zhang J, Liu H. Seeded Secondary Growth Synthesis of ZIF-8 Membranes Supported on α-Al2O3 Ceramic Tubes. J Inorg Mater. 2012;27:1105–1111.
crossref

87. Zhang J, Xia T, Zhao D, Cui Y, Yang Y, Qian G. In situ secondary growth of Eu(III)-organic framework film for fluorescence sensing of sulfur dioxide. Sens Actuators, B. 2018;260:63–69.
crossref

88. Li Y, Liang F, Bux H, Yang W, Caro J. Zeolitic imidazolate framework ZIF-7 based molecular sieve membrane for hydrogen separation. J Membr Sci. 2010;354:48–54.
crossref

89. Yoo Y, Lai Z, Jeong HK. Fabrication of MOF-5 membranes using microwave-induced rapid seeding and solvothermal secondary growth. Micropor Mesopor Mater. 2009;123:100–106.
crossref

90. Horcajada P, Serre C, Grosso D, et al. Colloidal Route for Preparing Optical Thin Films of Nanoporous Metal–Organic Frameworks. Adv Mater. 2010;21:1931–1935.
crossref

91. Yin J, Zhu G, Deng B. Graphene oxide (GO) enhanced polyamide (PA) thin-film nanocomposite (TFN) membrane for water purification. Desalination. 2016;379:93–101.
crossref

92. Freger V. Nanoscale Heterogeneity of Polyamide Membranes Formed by Interfacial Polymerization. Langmuir. 2003;19:4791–4797.
crossref

93. Rajesh , Ahuja T, Kumar D. Recent progress in the development of nano-structured conducting polymers/nanocomposites for sensor applications. Sens Actuators B. 2009;136:275–286.
crossref

94. Sara S, Patricia G, Carlos T, Joaquín C, Livingston AG. High flux thin film nanocomposite membranes based on metal-organic frameworks for organic solvent nanofiltration. J Am Chem Soc. 2013;135:15201–15208.
crossref

95. Yang MC, Liu TY. The permeation performance of polyacrylonitrile/ polyvinylidine fluoride blend membranes. J Membr Sci. 2003;226:119–130.
crossref

96. Ochoa NA, Masuelli M, Marchese J. Effect of hydrophilicity on fouling of an emulsified oil wastewater with PVDF/PMMA membranes. J Membr Sci. 2003;226:203–211.
crossref

97. Lin DJ, Chang CL, Lee CK, Cheng LP. Preparation and characterization of microporous PVDF/PMMA composite membranes by phase inversion in water/DMSO solutions. Eur Polym J. 2006;42:2407–2418.
crossref

98. Park JY, Acar MH, Akthakul A, Kuhlman W, Mayes A. Polysulfone-graft-poly (ethylene glycol) graft copolymers for surface modification of polysulfone membranes. Biomaterials. 2006;27:856–865.
crossref

99. Perez EV, Jr KJB, Ferraris JP, Musselman IH. Mixed-matrix membranes containing MOF-5 for gas separations. J Membr Sci. 2009;328:165–173.
crossref

100. Ordoñez MJC, Balkus KJ, Ferraris JP, Musselman IH. Molecular sieving realized with ZIF-8/Matrimid® mixed-matrix membranes. J Membr Sci. 2010;361:28–37.
crossref

101. Yeang QW, Sulong AB, Tan SH. Asymmetric membrane containing electrospun Cu-BTC/poly(vinyl alcohol) for pervaporation dehydration of 1,4-dioxane. Sep Purif Technol. 2018;192:240–252.
crossref

102. Shete M, Kumar P, Bachman JE, et al. On the direct synthesis of Cu(BDC) MOF nanosheets and their performance in mixed matrix membranes. J Membr Sci. 2018;549:312–320.
crossref

103. Goethem CV, Verbeke R, Mand Pfanmöller, et al. The role of MOFs in Thin-Film Nanocomposite (TFN) membranes. J Membr Sci. 2018;563:938–948.
crossref

104. Goethem CV, Verbeke R, Hermans S, Bernstein R, Vankelecom I. Controlled Positioning of MOFs in Interfacially Polymerized Thin-Film Nanocomposites. J Mater Chem A. 2016;4:16368–16376.
crossref

105. Ameloot R, Stappers L, Fransaer J, Alaerts L, Sels BF, Vos DED. Patterned Growth of MetalOrganic Framework Coatings by Electrochemical Synthesis. Chem Mater. 2009;21:2580–2582.
crossref

106. Feng Z, Zou X, Sun F, Hao R, Yuan J, Zhu G. Growth of preferential orientation of MIL-53(Al) film as nano-assembler. CrystEngComm. 2012;14:5487–5492.
crossref

107. Hailing G, Guangshan Z, Hewitt IJ, Shilun Q. “Twin copper source” growth of metal-organic framework membrane: Cu3(BTC)2 with high permeability and selectivity for recycling H2 . J Am Chem Soc. 2009;131:1646–1647.
crossref

108. Mitzi DB, Prikas MT, Chondroudis K. Thin-Film Deposition of Organic–Inorganic Hybrid Materials. Chem Mater. 2001;13:3283–3298.
crossref

109. Guerrero VV, Yoo Y, Mccarthy MC, Jeong HK. HKUST-1 membranes on porous supports using secondary growth. J Mater Chem. 2010;20:3938–3943.
crossref

110. Yoo Y, Jeong HK. Rapid fabrication of metal organic framework thin films using microwave-induced thermal deposition. Chem Commun. 2008;2008:2441–2443.
crossref

111. Aisheng H, Wei D, Jürgen C. Steam-stable zeolitic imidazolate framework ZIF-90 membrane with hydrogen selectivity through covalent functionalization. J Am Chem Soc. 2010;132:15562–15564.
crossref

112. Li Y, Liang F, Bux H, Feldhoff A. Molecular sieve membrane: supported metal-organic framework with high hydrogen selectivity. Angew Chem, Int Ed. 2010;3:548–551.
crossref

113. Mccarthy MC, Victor VG, Barnett GV, Hae-Kwon J. Synthesis of zeolitic imidazolate framework films and membranes with controlled microstructures. Langmuir. 2010;26:14636–14641.
crossref

114. Lind BHJM, Subramani A, Hoek XHAE. Effect of mobile cation on zeolite-polyamide thin film nanocomposite membranes. J Mater Res. 2009;24:1624–1631.
crossref

115. Sun CY, Qin C, Wang XL, et al. Zeolitic Imidazolate framework-8 as efficient pH-sensitive drug delivery vehicle. Dalton Trans. 2012;41:6906.
crossref

116. Bhattacharyya S, Pang SH, Dutzer MR, Lively RP, Nair S. Interactions of SO2-Containing Acid Gases with ZIF-8: Structural Changes and Mechanistic Investigations. J Phys Chem C. 2016;120:27221–27229.
crossref

117. Park KS, Ni Z, Côté AP, et al. Exceptional chemical and thermal stability of zeolitic imidazolate frameworks. Proc Natl Acad Sci U S A. 2006;103:10186–10191.
crossref

118. Aykac OH, Ozturk B. Gas separation characteristic of mixed matrix membrane prepared by MOF-5 including different metals. Sep Purif Technol. 2019;211:514–521.
crossref

119. Hou X, Stanley SL, Zhao M, et al. MOF-based C-doped coupled TiO2/ZnO nanofibrous membrane with crossed network connection for enhanced photocatalytic activity. J Alloys Compd. 2019;777:982–990.
crossref

120. Xu Y, Wen Y, Zhu W, Wu Y, Lin C, Li G. Electrospun nanofibrous mats as skeletons to produce MOF membranes for the detection of explosives. Mater Lett. 2012;87:20–23.
crossref

121. Cheng D, Zhao L, Li N, et al. Aluminum fumarate MOF/PVDF hollow fiber membrane for enhancement of water flux and thermal efficiency in direct contact membrane distillation. J Membr Sci. 2019;588:117204.
crossref

122. Erucar I, Keskin S. Computational assessment of MOF membranes for CH4/H2 separations. J Membr Sci. 2016;514:313–321.
crossref

123. Sun J, Li Q, Chen G, Duan J, Liu G, Jin W. MOF-801 incorporated PEBA mixed-matrix composite membranes for CO2 capture. Sep Purif Technol. 2019;217:229–239.
crossref

124. Ramos-Fernández EV, Garcia-Domingos M, Juan-Alcañiz J, Gascon J. MOFs meet monoliths: Hierarchical structuring metal organic framework catalysts. Appl Catal , A. 2011;391:261–267.
crossref

125. Deng R, Han W, Yeung KL. Confined PFSA/MOF composite membranes in fuel cells for promoted water management and performance. Catal Today. 2019;331:12–17.
crossref

126. Cheng X, Jiang Z, Cheng X, et al. Bimetallic metal-organic frameworks nanocages as multi-functional fillers for water-selective membranes. J Membr Sci. 2018;545:19–28.
crossref

127. Yang S, Zou Q, Wang T, Zhang L. Effects of GO and MOF@GO on the permeation and antifouling properties of cellulose acetate ultrafiltration membrane. J Membr Sci. 2019;569:48–59.
crossref

128. Kadhom M, Deng B. Metal-organic frameworks (MOFs) in water filtration membranes for desalination and other applications. Appl Mater Today. 2018;11:219–230.
crossref

129. Lee JY, She Q, Huo F, Tang CY. Metal–organic framework-based porous matrix membranes for improving mass transfer in forward osmosis membranes. J Membr Sci. 2015;492:392–399.
crossref

130. Ma D, Peh SB, Han G, Chen SB. Thin-Film Nanocomposite (TFN) Membranes Incorporated with Super-Hydrophilic Metal-Organic Framework (MOF) UiO-66: Toward Enhancement of Water Flux and Salt Rejection. ACS Appl Mater Interfaces. 2017;9:7523–7534.
crossref

131. Xu Y, Gao X, Wang X, Wang Q, Ji Z. Highly and Stably Water Permeable Thin Film Nanocomposite Membranes Doped with MIL-101 (Cr) Nanoparticles for Reverse Osmosis Application. Materials. 2016;9:870.
crossref

132. Xinlei L, Nilay Keser D, Zhentao W, Kang L. Highly Water-Stable Zirconium Metal-Organic Framework UiO-66 Membranes Supported on Alumina Hollow Fibers for Desalination. J Am Chem Soc. 2015;137:6999–7002.
crossref

133. Nightingale ERJ. Phenomenologocal Theory of Ion Solvation. Effective Radii of Hydrated Ions. J Phys Chem. 1958;9:566–567.


134. Fu F, Wang Q. Removal of heavy metal ions from wastewaters: A review. J Environ Manage. 2011;92:407–418.
crossref

135. Yuan J, Hung W, Zhu H, et al. Fabrication of ZIF-300 membrane and its application for efficient removal of heavy metal ions from wastewater. J Membr Sci. 2019;572:20–27.
crossref

136. Jamshidifard S, Koushkbaghi S, Hosseini S, et al. Incorporation of UiO-66-NH2 MOF into the PAN/chitosan nanofibers for adsorption and membrane filtration of Pb(II), Cd(II) and Cr(VI) ions from aqueous solutions. J Hazard Mater. 2019;368:10–20.
crossref

137. Efome JE, Rana D, Matsuura T, Lan CQ. Experiment and modeling for flux and permeate concentration of heavy metal ion in adsorptive membrane filtration using a metal-organic framework incorporated nanofibrous membrane. Chem Eng J. 2018;352:737–744.
crossref

138. Yin N, Wang K, Wang L, Li Z. Amino-functionalized MOFs combining ceramic membrane ultrafiltration for Pb (II) removal. Chem Eng J. 2016;306:619–628.
crossref

139. Mimura K, Takahashi Y, Takanashi S, Deguchi H. The behaviour of organic matter in hybrid water treatment system. Sep Purif Technol. 2019;221:385–392.
crossref

140. Jin M, Lin Y, Liao Y, Tan C, Wang R. Development of highly-efficient ZIF-8@PDMS/PVDF nanofibrous composite membrane for phenol removal in aqueous-aqueous membrane extractive process. J Membr Sci. 2018;568:121–133.
crossref

141. Li Q, Liu Q, Zhao J, et al. High efficient water/ethanol separation by a mixed matrix membrane incorporating MOF filler with high water adsorption capacity. J Membr Sci. 2017;544:68–78.
crossref

142. Mao H, Zhen H, Ahmad A, Zhang A, Zhao Z. In situ fabrication of MOF nanoparticles in PDMS membrane via interfacial synthesis for enhanced ethanol permselective pervaporation. J Membr Sci. 2019;573:344–358.
crossref

143. Gao B, Jiang Z, Zhao M, et al. Enhanced dehydration performance of hybrid membranes by incorporating lanthanide-based MOFs. J Membr Sci. 2018;546:31–40.
crossref

144. Sánchez NC, Guzmán-Mar JL, Hinojosa-Reyes L, Palomino GT, Cabello CP. Carbon composite membrane derived from MIL-125-NH2 MOF for the enhanced extraction of emerging pollutants. Chemosphere. 2019;231:510–517.
crossref

145. Kasik A, Lin YS. Organic solvent pervaporation properties of MOF-5 membranes. Sep Purif Technol. 2014;121:38–45.
crossref

146. Kang C, Lin Y, Huang Y, et al. Synthesis of ZIF-7/chitosan mixed-matrix membranes with improved separation performance of water/ethanol mixtures. J Membr Sci. 2013;438:105–111.
crossref

147. Tan Y, Sun Z, Meng H, et al. A new MOFs/polymer hybrid membrane: MIL-68(Al)/PVDF, fabrication and application in high-efficient removal of p-nitrophenol and methylene blue. Sep Purif Technol. 2019;215:217–226.
crossref

148. Ragab D, Gomaa HG, Sabouni R, Salem M, Ren M, Zhu J. Micropollutants removal from water using microfiltration membrane modified with ZIF-8 metal organic frameworks (MOFs). Chem Eng J. 2016;300:273–279.
crossref

Fig. 1
Preparation of MOFs modified membrane by LBL method.
/upload/thumbnails/eer-2019-435f1.gif
Fig. 2
Process of secondary growth method.
/upload/thumbnails/eer-2019-435f2.gif
Fig. 3
Process of Interface polymerization method.
/upload/thumbnails/eer-2019-435f3.gif
Fig. 4
Process of cohybridization method.
/upload/thumbnails/eer-2019-435f4.gif
Fig. 5
An overview on application of MOFs and MOFs modified membranes.
/upload/thumbnails/eer-2019-435f5.gif
Editorial Office
464 Cheongpa-ro, #726, Jung-gu, Seoul 04510, Republic of Korea
TEL : +82-2-383-9697   FAX : +82-2-383-9654   E-mail : eer@kosenv.or.kr

Copyright© Korean Society of Environmental Engineers.        Developed in M2PI
About |  Browse Articles |  Current Issue |  For Authors and Reviewers